AISI 3115 15CrNi6 Seamless Steel Pipe


1: DIN 1.5919 Steel Introduction

  15CrNi6/1.5919  is a low-alloy steel containing chromium and Nickel as strengthening elements.It has good mechanical property for highly strained parts and good toughness at core tensile strength of 900 - 1200 N/mm2. This material is generally used driving bevel gears, crown wheels, gears, shafts, bolts for automotive and gear components.

(25) (10)

1.5919 steel Stock in warehouse


2: 1.5919 Quality Standard

EN10250-3 2000 ENG  Open die forging alloy steel.pdf


3: DIN 1.5919 Steel Equivalent

Country China Japan Germany USA British
Standard

GB

GB/T 3077

JIS 

JIS G4105/JIS

DIN (W-Nr.)
EN 10250
ASTM A29

BS

BS 970

Grade / / 15CrNi6 / 1.5919 3115 /


4: DIN 1.5919 Steel Chemical Composition

Grade C Si Mn P S Cr Mo Ni
1.5919 0.14-0.19 0.4 0.4-0.6 0.025 0.035 1.4-1.7 / 1.4-1.7
3115 0.13-0.18 0.2-0.35 0.4-0.6 0.04 0.04 1.4-1.7 / 1.4-1.7


5: DIN 1.5919 Steel Mechanical Properties

 The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, please kindly contact the salesman.


6: DIN 1.5919 Steel Overviews

Size Round Dia 6-1200mm
Plate/Flat/Block Thickness
6mm-500mm
Width
20mm-1000mm
Heat treatment Normalized ; Annealed ; Quenched ; Tempered
Surface condition Black; Peeled; Polished; Machined; Grinded; Turned; Milled
Delivery condition Forged; Hot rolled; Cold drawn
Test Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc.
Payment terms T/T;L/C;/Money gram/ Paypal
Trade terms FOB; CIF; C&F; etc..
Delivery time 30-45 days


7: DIN 1.5919 Steel Application

 1.5919 alloy steels are used for driving bevel gears, crown wheels, gears, shafts, bolts for automotive and gear components.


8: DIN 1.5919 Steel Heat Treatment

Normalizing For 15CrNi6

Nominal normalizing temperature:850-880°C

Hold the temperature for several hours

Cooling in the air
Annealing  For 15CrNi6

Nominal Annealing temperature:650-700°C

Cool slowly in the furance

Maximum Brinell hardness of 229
Hardening and Tempering(QT)  For 15CrNi6

Nominal Hardening temperature:820-870°C

Hold at this temperature then quench in oil or water

Tempering  as soon as possible when the temperature low to ambient

Heat uniformly to the suitable temperature.

keep the material out of the furnace ,then cool in the air
Mechanical Property( for reference only)

Tensile strength: 880-1100MPa

Yield point: 635MPa

Percentage reduction of area after fracture: 40%

Elongation after fracture: 11%

Impact test (+20°C):  Longitud – 40~60J

Get In Touch
SPECIALIZING IN SPECIAL STEEL SMELTING AND FORGING

About Us

Hunan Qilu Metal is one of the professional steel manufacturers and exporters in China, with multiple certificates such as ISO9001. Our products can be produced according to customer requirements, with a small minimum order quantity and affordable prices.

Quick Links

Product Category

Contact Us

Tel:+86-731-85185765
Email:enquiry@qilumetal.com
Address:Room 2832, Building B3 to B6, Taskin Urban Plaza, No. 18 Xiangfu Middle Road,Yuhua District, Changsha City
Copyright 2023 © Hunan Qilu Metal Co.,Ltd.  All rights reserved.  Support by LeadongSitemapPrivacy Policy