DIN 16NiCr4/1.5714 EN351/637M17 Steel Alloy Plate/ Flat Bar
1: DIN 16NiCr4 Steel Introduction
16NiCr4 Alloy steel is a low carbon case hardening steel which has at least 0.6Cr%,0.8%Ni as strengthening elements. It has a low-medium hardenability with good core resistance up to a thickness of about 50 mm, and had good machinability in the annealed condition.16NiCr4 is generally supplied in the annealed condition with Max hardness 217HB.
16NiCr4 steel Stock in warehouse
2: 16NiCr4 Quality Standard
EN10250-3 2000 ENG Open die forging alloy steel.pdf
3: DIN 16NiCr4 Steel Equivalent
| Country | China | Japan | Germany | USA | British |
| Standard | GB GB/T 3077 | JIS JIS G4105/JIS | DIN (W-Nr.) EN 10250 | ASTM A29 | BS BS 970 |
| Grade | / | / | 16NiCr4 / 1.5714 | / | EN351 / 637M17 |
4: DIN 16NiCr4 Steel Chemical Composition
| Grade | C | Si | Mn | P | S | Cr | Ni |
| 16NiCr4 | 0.13-0.19 | 0.70-1.00 | ≤ 0.4 | ≤ 0.025 | ≤ 0.035 | 0.60-1.00 | 0.80-1.10 |
5: DIN 16NiCr4 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, please kindly contact the salesman.
6: DIN 16NiCr4 Steel Overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm | |
| Width 20mm-1000mm | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
7: DIN 16NiCr4 Steel Application
16NiCr4 Alloy steel is a case-hardening steel widely used for high-strength core parts, structural parts subject to abrasion and variable loads typically used for small-sized parts, such as loaded gears, screws, pins, shafts, pivots, machine parts, cars and engines.
8: DIN 16NiCr4 Steel Heat Treatment
Forging
16NiCr4 Alloy steel forging temperature:900 – 1150°C, cooled as slowly as possible in still air or in the sand after forged.
Heat Treatment
Normalizing: 870 – 890°C, Cooling in air
Soft Annealing:680 – 720°C, Cooling in the furnace
Carburizing:880-980°C
Core-hardening:850-890°C,oil-polymer salt bath
Case-hardening:780-820°C,oil-polymer salt bath
Carbonitriding:860-930°C/Gas
Tempering:150-200°C
Surface Hardness
Treated to improve wearability(+S): Max 255HB
Soft annealed(+A): Max 217HB
Treated to hardness range(+TH):166-217HB
Treated to ferrite-pearlite structure and hardness range(+FP):156-207HB
9: Delivery condition
Usually the delivery condition is hot forged or rolled, annealed/QT, rough turned/Black surface for hot forged rolled bar.
The delivery condition is usually hot rolled, annealed/QT, Black surface for hot forged or hot rolled bar.
But for hot forged or hot rolled plate, usually the delivery condition is hot forged, annealed/QT, milled surface/Black surface or hot rolled, annealed/QT, black surface.