SKH55 1.3243 M35 High Speed Steel Flat Bar
1: AISI M35 Steel Introduction
M35 steel is a medium-alloyed high speed tool steel. It is also known as HSSE or HSS-E which is similar to M2, but with 5% cobalt added, which makes better hot hardness and wear resistance. AISI /ASTM A600 M35 high speed steel is suitable for heat treatment up to 66 HRC, and also offers excellent cutting performance and offers excellent cutting performance. AISI high speed Tool Steel M35 is suitable for broaches, taps, milling, reamers, hobs, shapers cutters, saws ,etc.
M35 steel Stock in warehouse
2: A681 Quality Standard
ASTM-A681-2008 ENG Standard-Specification-for-Tool-Steel-Alloy.pdf
3: AISI M35 Steel Equivalent
| Country | USA | German | Japan |
| Standard | ASTM A681 | DIN EN ISO 4957 | JIS G4403 |
| Grade | M35 | 1.3243 | SKH55 |
4: AISI M35 Steel Chemical Composition
| Grade | C | Si | Mn | P | S | Cr | Mo | V | W | Co |
| M35 | 0.82-0.95 | 0.2-0.45 | 0.15-0.4 | 0.03 | 0.03 | 3.8-4.5 | 4.75-5.25 | 1.75-2.15 | 5.5-6.5 | 4.6-5 |
| 1.3243 | 0.87-0.95 | 0.45 | 0.4 | 0.03 | 0.03 | 3.8-4.5 | 4.7-5.2 | 1.7-2.1 | 5.9-6.7 | 4.5-5 |
| SKH55 | 0.87-0.95 | 0.45 | 0.4 | 0.03 | 0.03 | 3.8-4.5 | 4.7-5.2 | 1.7-2.1 | 5.9-6.7 | 4.5-5 |
5: AISI M35 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
6: AISI M35 Steel Overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm | |
| Width 20mm-1000mm | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
7: AISI M35 Steel Application
M35 are used for cutting tools such as cutting tools including broaches, milling cutters, reamers, end mills and saw blades. It is also a good quality wear resistant HSS grade for cold work area. Steel M35 is also suitable for cold work applications, where exacting demands are imposed on wear resistance. The steel possesses an admirable combination of wear resistance and toughness and in these respects superior to the high alloyed cold work steels.
8: AISI M35 Steel Heat Treatment
Soft-annealing 850°C – 900°C / 1560°F – 1650°F, slow cooling 10°C / 18°F/h to 700°C / 1290°F, hardness max 260 Brinell.
Stress relieving 600°C – 700°C / 1120°F – 1290°F, approx. 2 hours at temperature, slow cooling to 500°C / 930°F.
Hardening with preheating in two steps 450°C – 500°C / 840°F – 930°F, 850°C – 900°C / 1560°F – 1650°F and austenitizing at 1050°C – 1220°C / 1920°F – 2230°F. Quenching to about 550°C / 1022°F then cool in air to hand warm
Tempering at 560°C / 1040°F or higher 2 times for at least 1 hour at full temperature is recommended.
9: Delivery Condition
For hot forged bar, usually the delivery condition is hot forged, annealed rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed, Black surface.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.