DIN 14NiCr14 3415 EN36/655M13 Carbon Steel Pipe/Tube
1: AISI 3415 Steel Introduction
3415 (3310) is a nickel-chromium-molybdenum based case hardening engineering steel which is specifically designed for carburising. It is used specifically in heavy duty and highly stressed applications due to its hardenability, toughness and high core strength and it also offers excellent fatigue resistance.
3415 steel Stock in warehouse
2: 3415 Quality Standard
3: AISI 3415 Steel Equivalent
| Country | China | Japan | Germany | USA | British |
| Standard | GB/T 3077 | JIS G4105/JIS | DIN (W-Nr.) EN 10250 | AISI/ASTM ASTM A29 | BS 970 |
| Grade | / | / | 14NiCr14 / 1.5752 | 3310 / 3415 | EN36 / 655M13 |
4: AISI 3415 Steel Chemical Composition
| Grade | C | Si | Mn | P | S | Cr | Ni |
| EN36 / 655M13 | 0.12-0.18 | 0.10-0.35 | 0.30-0.60 | 0.05 | 0.05 | 0.60-1.10 | 3.00-3.75 |
| 3310 / 3415 | 0.10-0.20 | 0.15-0.30 | 0.30-0.60 | 0.04 | 0.05 | 0.60-0.95 | 2.75-3.25 |
| 14NiCr14 / 1.5752 | 0.14-0.20 | ≤ 0.40 | 0.40-0.70 | 0.025 | 0.035 | 0.60-0.90 | 3.00-3.50 |
5: AISI 3415 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, please kindly contact the salesman.
6: AISI 3415 Steel Overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm | |
| Width 20mm-1000mm | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
7: AISI 3415 Steel Application
AISI 3415 highly stressed components in automotive construction, and for general engineering purposes, e. g. gears, crankshafts, gear shafts. Its most common applications are for gears, pinions, reducers, speed boxes, cams, bolts and ball joints.
8: AISI 3415 Steel Heat treatment
Hardening
Case-hardening: 880-980oC, oil (water), warm bath at 160-250oC. Carburising: Salt bath at 580-650oC, case-hardening box, air.
Direct hardening: 880-890oC, oil, hot bath at 160-250oC.
Core refining: 840-880oC, oil, hot bath at 160-250oC.
Case refining: 780-820oC, oil, hot bath at 160-250oC.
Normalizing
Normalizing temperature: 850 – 880oC.
Tempering
Tempering temperature: 150 – 200oC.
Forging
Hot forming temperature: 1050-850oC.