SKH51 1.3343 M2 Carbon Steel Flat


1: AISI M2 Steel Introduction

  AISI M2 Tool Steel is molybdenum based high-speed steel in tungsten-molybdenum series. HSS grade steel M2 is a medium alloyed high speed steel which has good machinability. The H-SS M2 chemical composition gives a good combination of well-balanced toughness, wear resistance and red hardness properties. Widely used for cutting tools such as twist drills, taps, milling cutters, saws, knives etc. Also commonly used in cold work punches and dies and cutting applications involving high speed and light cuts.

   Grade M2 High Speed Steel is by far the most popular high speed steel replacing high speed steel grade T1 in most applications because of its superior properties and relative economy.

                        1.2379 M2

M2 steel Stock in warehouse


2: A600 Quality Standard

ASTM-A600-1992-ENG Standard-Specification-for-High-Speed-Tool-Steel.pdf


3: AISI M2 Steel Equivalent

Country Japan Germany Britain USA
Standard JIS G4403
DIN EN ISO 4957 BS 4659 ASTM A600
Grade SKH51
1.3343 / M2


4: AISI M2 Steel Chemical Composition

ASTM A600 C Mn P S Si Cr V Mo W
M2 0.78-0.88
0.15-0.40
0.03-0.03
0.20-0.45
3.75-4.50
1.75-2.20
4.50-5.50
5.50-6.75
1.3343 0.86-0.94


0.45
3.80-4.50
1.70-2.10
4.70-5.20
5.90-6.70
SKH51 0.80-0.88
0.40
0.03-0.03
0.45
3.80-4.50
1.70-2.10
4.70-5.20
5.90-6.70


5: AISI M2 Steel Mechanical Properties

   The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.


6: AISI 40Cr Steel Overviews

Size Round Dia 6-1200mm
Plate/Flat/Block Thickness
6mm-500mm
Width
20mm-1000mm
Heat treatment Normalized ; Annealed ; Quenched ; Tempered
Surface condition Black; Peeled; Polished; Machined; Grinded; Turned; Milled
Delivery condition Forged; Hot rolled; Cold drawn
Test Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc.
Payment terms T/T;L/C;/Money gram/ Paypal
Trade terms FOB; CIF; C&F; etc..
Delivery time 30-45 days


7: AISI M2 Steel Application

  Typical applications for M2 high speed steel are twist drills, reamers, broaching tools, taps, milling tools, metal saws. M2 is suitable for cold forming tools such as extrusion rams and dies, also widely used in all kinds of cutting tools, knife and punches and die applications, plastic moulds with elevated wear resistance and screws.


8: AISI M2 Steel Heat Treatment

Anneal

   Heat to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to 900° F, air cool to room temperature. Approximate annealed hardness 241 Maximum Brinell.

   Stress Relief of Unhardened Material: Heat slowly to 1200 to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.

Harden

   Heat slowly to 1550° F, soak thoroughly, heat to 1850° F, soak thoroughly. Soak time in the furnace varies from a few minutes to 15 minutes, depending tool size, heat capacity of the furnace, and the size of the charge. – Heat to 2150 to 2200° F for max. toughness and minimum distortion. – Heat to 2250 to 2275° F for max. hardness and abrasion resistance.

Quench

   For full hardness, oil quench to 150-200° F. Air quench to 150° F. When quenching in hot salt maintain the quench just above the Ms temperature. After equalizing withdraw parts from the hot salt and air cooled to 150° F.

Temper

   Double temper is mandatory, three tempers are sometimes preferred. Soak for 2 hours per inch of thickness. Air cool to room temperature between tempers. The best tempering range for hardness, strength and toughness is 1000 to 1050° F.


9: Delivery Condition

For hot forged bar, usually the delivery condition is hot forged, annealed rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed, Black surface.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.

Get In Touch
SPECIALIZING IN SPECIAL STEEL SMELTING AND FORGING

About Us

Hunan Qilu Metal is one of the professional steel manufacturers and exporters in China, with multiple certificates such as ISO9001. Our products can be produced according to customer requirements, with a small minimum order quantity and affordable prices.

Quick Links

Product Category

Contact Us

Tel:+86-731-85185765
Email:enquiry@qilumetal.com
Address:Room 2832, Building B3 to B6, Taskin Urban Plaza, No. 18 Xiangfu Middle Road,Yuhua District, Changsha City
Copyright 2023 © Hunan Qilu Metal Co.,Ltd.  All rights reserved.  Support by LeadongSitemapPrivacy Policy