18CrNiMo7-6 Hot Rolled Alloy Steel Bar
1: 18CrNiMo7-6 Steel Introduction
18CrNiMo7-6 structural steel is a widely used alloy structural steel in Europe with high flexural strength and wear resistance. The heart of this steel also has high hardness and toughness, resulting in high overall mechanical properties. Its chemical composition includes the elements carbon, silicon, manganese, phosphorus, sulfur, chromium, nickel, and molybdenum, with specific contents ranging from 0.15% to 0.21% of other elements.
18CrNiMo7-6 Steel Stock in Warehouse
2: 18CrNiMo7-6 Quality Standard
18CrNiMo7-6 steel according to EN 10250.
3: 18CrNiMo7-6 Steel Equivalent
| Country | China | Japan | Germany | USA | British |
| Standard | GB/T 3077 | JIS G4105 | DIN (W-Nr.) EN 10250 | AISI/ASTM/SAE ASTM A29 | BS 970 |
| Grade | 17CrNiMo6 | / | 18CNirMo7-6 / 1.6587 | 4815 | / |
4: 18CrNiMo7-6 Steel Chemical Composition
| Grade | C | Si | Mn | P | S | Cr | Mo | Ni |
| 4815 | 0.13-0.18 | 0.15-0.35 | 0.40-0.60 | 0.035 | 0.04 | / | 0.20-0.30 | 3.25-3.75 |
18CrNiMo7-6/ 1.6587 | 0.15-0.21 | 0.40 | 0.50-0.90 | 0.025 | 0.015 | 1.50-1.80 | 0.25-0.35 | 1.40-1.70 |
| 17CrNiMo6 | 0.15-0.20 | 0.40 | 0.40-0.60 | 0.035 | 0.035 | 1.50-1.80 | 0.25-0.35 | 1.40-1.70 |
5: 18CrNiMo7-6 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
6: 18CrNiMo7-6 Steel Overviews
Size | Round | Dia 6-1200mm |
Plate/Flat/Block | Thickness | |
Width | ||
Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
Delivery condition | Forged; Hot rolled; Cold drawn | |
Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
Payment terms | T/T;L/C;/Money gram/ Paypal | |
Trade terms | FOB; CIF; C&F; etc.. | |
Delivery time | 30-45 days | |
7: 18CrNiMo7-6 Steel Application
18CrNiMo7-6 is widely used in the machinery manufacturing industry, especially in the field of manufacturing large gears, transmission shafts, turbine shafts and other high-load and high-speed working parts. The alloy steel has good wear resistance and impact resistance, and can meet the requirements of use in a variety of complex working conditions.
8: 18CrNiMo7-6 Steel Heat Treatment
Hot Forging
To be carried out between 1150°C and 1150°C to ensure that the material has good plasticity and uniform heating.
Annealing
Annealing temperatures range from 650°C to 700°C. This step helps to reduce the hardness of the material and improve its plasticity and toughness.
Carburizing
Carburizing temperatures range between 880°C and 980°C. This process increases the carbon content on the surface of the steel part, thus improving its hardness and wear resistance.
Hardening
It consists of two stages, i.e., Hardening I (heart hardening) is carried out at 830°C to 870°C and Hardening II (surface hardening) is carried out at 780°C to 820°C, usually using oil as the cooling medium.
Tempering
Tempering is carried out at temperatures between 150°C and 200°C. Tempering is done to stabilize the material and reduce internal stresses generated during heat treatment.
9: 18CrNiMo7-6 Steel Tolerance
Diameter(mm) | Tolerance | ||
Forged Steel Round Bar | 80-600 | Black Surface:0~+5 | Rough Machined or Turned:0~+3 |
650-1200 | Black Surface:0~+15 | Rough Machined or Turned:0~+3 | |
Hot Rolled Steel Round Bar | 16-310 | Black Surface:0~+1 | Peeled:H11 |
Cold Drawn Steel Round Bar | 6-100 | Black Surface:H11 | Peeled:H11 |
10: Delivery Condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed or QT, black surface or rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed or QT, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed or QT, black surface.