H11 SKD6 BH11 1.2343 X37CrMoV5-1 4Cr5MoV Hot Work Tool Steel
1: AISI H11 Steel Introduction
AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. Chromium hot-work tool steels are designated as group H steels according to the AISI classification system, and specified in ASTM A681standard. The most commonly used chromium hot-work steels are H11 tool steel, h12 tool steel, and H13 steel, within the series from H1 to H19.
H11 tool steel is a deep-hardening, air-hardening steel and H11 alloy steel could be deep hardened by heat treatment and air-quenching. That gives minimal size change during heat treatment. H11 how work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 Steel Stock In Warehouse
2: H11 Quality Standard
ASTM-A681-2008 ENG Standard-Specification-for-Tool-Steel-Alloy.pdf
3: AISI H11 Steel Equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
| Grade | 4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
4: AISI H11 Steel Chemical Composition
| Grade | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| H11/T20811 | 0.35 | 0.45 | 0.20 | 0.60 | 0.03 | 0.03 | 0.80 | 1.25 | 4.75 | 5.50 | 0.30 | 0.60 | 1.10 | 1.60 |
| 1.2343/ X37CrMoV5-1 | 0.28 | 0.35 | 0.10 | 0.40 | / | / | 0.80 | 1.20 | 2.70 | 3.20 | 0.40 | 0.70 | 1.10 | 1.50 |
| SKD6 | 0.32 | 0.42 | / | 0.50 | 0.03 | 0.03 | 0.80 | 1.20 | 4.50 | 5.50 | 0.30 | 0.50 | 1.00 | 1.50 |
| BH11 | 0.32 | 0.40 | / | 0.40 | 0.35 | 0.35 | 0.85 | 1.15 | 4.75 | 5.25 | 0.30 | 0.50 | 1.25 | 1.75 |
5: AISI H11 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
6: AISI H11 Steel Overviews
| Size | Round | Dia 6-1200mm | |
| Plate/Flat/Block | Thickness 6mm-500mm | ||
| Width 20mm-1000mm | |||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | ||
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | ||
| Delivery condition | Forged; Hot rolled; Cold drawn | ||
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | ||
| Payment terms | T/T;L/C;/Money gram/ Paypal | ||
| Trade terms | FOB; CIF; C&F; etc.. | ||
| Packing | standard packages or as per customers request. | ||
| Delivery time | 30-45 days | ||
7: H11 Steel Application
AISI H11 tool steel are suitable for hot punches, die casting dies, forging dies, hot shear blades, hot gripper dies, and extrusion tooling, dies, liners, die holder backers, aluminium extrusion mold, copper alloy mold, stainless products mold, plastic mould tool, hot extrusion mould etc.
8: H11 Steel Heat Treatment
Annealing
Slowly heat to 843 – 898(1550-1650 F) then slowly Cool to 538(1000) in heat treatment furnace. Then frosty in make public. After annealing hardness HBS: 235 Max
Hardening
H11 steel having enormously high hardenability and should be hardened by cooling in yet appearance. The use of a salt bath or controlled mood furnace is desirable to minimize decarburization, and if not user-simple, pack hardening in spent arena coke is suggested. The temperature employed is usually 1800-1850F, depending upon size section.
Quenching
Quenching temperature / ℃ | salt bath furnace: 996
Quenching temperature / ℃ | controlled atmosphere furnace: 1010
The heat preservation time/min: 5 ~ 15
Quenching medium: air cooling.
Tempering
Tempering temperature / : 552
After tempering hardness HRC or future: 52
9: H11 Steel Tolerance
Diameter(mm) | Tolerance | ||
Forged Steel Round Bar | 80-600 | Black Surface:0~+5 | Rough Machined or Turned:0~+3 |
650-1200 | Black Surface:0~+15 | Rough Machined or Turned:0~+3 | |
Hot Rolled Steel Round Bar | 16-310 | Black Surface:0~+1 | Peeled:H11 |
Cold Drawn Steel Round Bar | 6-100 | Black Surface:H11 | Peeled:H11 |
10: Delivery Condition
For hot forged bar, usually the delivery condition is hot forged, annealed rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed, Black surface.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.