Product Description
Steel Flat Cr12MoV 1.2601 D5 Cold Work Tool Steel Plate
1: DIN 1.2601 Steel Introduction
DIN 1.2601 is a Cold work tool alloy steel material grade.it is shock resisting steel. Digital Grade material number 1.2601 use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold. Our Tool Steel material 100 % ultrasonic tested with good price. Small size steel products make by hot rolled, large size steel products make by forging. 1.2601 with is equivalent Belong to DIN.
Cr12MoV Steel Stock In Warehouse
2: DIN 1.2601 Quality Standard
GBT 1299-2000-Chinese Alloy Tool Steels.pdf
3: DIN 1.2601 Steel Equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
| Grade | Cr12MoV | / | 1.2601 | D5 | / |
4: DIN 1.2601 Steel Chemical Composition
| Grade | C | Mn | P | S | Si | W | V | Cr | ||||||
| DIN 1.2601 | 1.55 | 1.75 | 0.20 | 0.40 | 0.03 | 0.03 | 0.25 | 0.40 | 0.40 | 0.6. | 0.1 | 0.50 | 11.0 | 12.0 |
5: DIN 1.2601 Steel Mechanical Properties
| Grade | Tensile strength | Yield strength | Elongation | Reduction | Impact Value | Hardness |
| DIN 1.2601 | 488 (≥)MPa | / | 12% | 31% | 31J | Annealing 225 HB max, Q+T: 58-63 HRc |
6: DIN 1.2601 Steel Overviews
| Size | Round | Dia 6-1200mm | |
| Plate/Flat/Block | Thickness 6mm-500mm | ||
| Width 20mm-1000mm | |||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | ||
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | ||
| Delivery condition | Forged; Hot rolled; Cold drawn | ||
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | ||
| Payment terms | T/T;L/C;/Money gram/ Paypal | ||
| Trade terms | FOB; CIF; C&F; etc.. | ||
| Packing | Standard Packages, or as Customers Request | ||
| Delivery time | 30-45 days | ||
7: DIN 1.2601 Steel Application
DIN 1.2601 is suitable for applications High alloyed CrMoV steel for cutting tool and cold work tool steel.
8: DIN 1.2601 Steel Heat Treatment
Annealing:
Temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255.
Quenching:
Hardening temperature/℃: 980~1010, Quenching in oil or air.
Tempering:
Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58.
Normalizing:
at Normalizing temperature, then cool in furnace.
9: DIN 1.2601 Steel Tolerance
Diameter(mm) | Tolerance | ||
Forged Steel Round Bar | 80-600 | Black Surface:0~+5 | Rough Machined or Turned:0~+3 |
650-1200 | Black Surface:0~+15 | Rough Machined or Turned:0~+3 | |
Hot Rolled Steel Round Bar | 16-310 | Black Surface:0~+1 | Peeled:H11 |
Cold Drawn Steel Round Bar | 6-100 | Black Surface:H11 | Peeled:H11 |
10: Delivery Condition
For hot forged bar, usually the delivery condition is hot forged, annealed rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed, Black surface.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.