AISI D2 SKD11 1.2379 Tool Steel Plate
1: D2 Steel Introduction
Cold-work tool steels include the high-carbon, high-chromium steels or group D steels, D2 is the most popular one,these steels all contain 1.5% to 2.35% of carbon and 12% of chromium. D2 steel is an air hardening, high-carbon, high-chromium tool steel. It has high wear and abrasion resistant properties. It is heat treatable and will offer a hardness in the range 55-62 HRC, and is machinable in the annealed condition. D2 steel shows little distortion on correct hardening. D2 steel’s high chromium content gives it mild corrosion resisting properties in the hardened condition.
If customer need better machinability, we recommend A2, because A2 has a chromium content of 5% and is more readily machinable.
D2 Steel Stock In Warehouse
2: D2 Quality Standard
ASTM-A681-2008 ENG Standard-Specification-for-Tool-Steel-Alloy.pdf
3: D2 Steel Equivalent
Country | China | Japan | Germany | USA |
Standard | GB/T 1299 | JIS G4404 | EN ISO 4957 | ASTM A681 |
Grade | Cr12Mo1V1 | SKD11 | 1.2379 | D2 |
4: D2 Steel Chemical Composition
Grade | C | Si | Mn | P | S | Cr | Mo | V |
SKD11 | 1.4-1.6 | 0.4 | 0.6 | 0.03 | 0.03 | 11-13 | 0.8-1.2 | 0.2-0.5 |
1.2379 | 1.45-1.6 | 0.15-0.6 | 0.2-0.6 | 0.03 | 0.03 | 11-13 | 0.7-1.0 | 0.7-1.0 |
D2 | 1.4-1.6 | 0.1-0.6 | 0.1-0.6 | 0.03 | 0.03 | 11-13 | 0.7-1.2 | 0.5-1.1 |
5: D2 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
6: D2 Steel Overviews
| Size | Round | Dia 6-1200mm | |
| Plate/Flat/Block | Thickness 6mm-500mm | ||
| Width 20mm-1000mm | |||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | ||
| Heat teatment | Normalized ; Annealed ; Quenched ; Tempered | ||
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | ||
| Delivery condition | Forged; Hot rolled; Cold drawn | ||
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | ||
| Payment terms | T/T;L/C;/Money gram/ Paypal | ||
| Trade terms | FOB; CIF; C&F; etc.. | ||
| Packing | Standard Packages, or as Customers Request | ||
| Delivery time | 30-45 days | ||
7: D2 Steel Application
D2 tool steel are as below:Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
8: D2 Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815℃ (1500°F) and then temperature can be increased to 1010oC (1850°F). They are then held at 1010oC (1850°F) for 20 to 45 minutes and air cooled (air quenched).
Annealing
Annealing of D2 tool steels material should be done at 871 to 898°C (1600 to 1650°F) followed by slow furnace cooling at 4.4°C (40°F) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
Stress Relieving
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
Hardening
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
Quenching
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
Tempering
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204°C (400°F) for achieving Rockwell C hardness of 61 and at 537°C (1000°F) for a Rockwell C hardness of 54.
9: D2 Steel Tolerance
Diameter(mm) | Tolerance | ||
Forged Steel Round Bar | 80-600 | Black Surface:0~+5 | Rough Machined or Turned:0~+3 |
650-1200 | Black Surface:0~+15 | Rough Machined or Turned:0~+3 | |
Hot Rolled Steel Round Bar | 16-310 | Black Surface:0~+1 | Peeled:H11 |
Cold Drawn Steel Round Bar | 6-100 | Black Surface:H11 | Peeled:H11 |
10: Delivery Condition
For hot forged bar, usually the delivery condition is hot forged, annealed rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed, Black surface.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.