60CrMnA SUP9A 5160 Spring Steel
1: AISI 5160 Steel Introduction
5160 steel, also known as AISI 5160 Alloy Spring Steel, is a high carbon and chromium alloy (0.6% carbon content, 0.9% chromium content and 1% manganese content). The steel offers significant levels of toughness, impressive resistance to fatigue and a high degree of ductility.
5160 steel Stock in warehouse
2: 5160 Quality Standard
3: AISI 5160 Steel Equivalent
| Country | China | Japan | BS | USA |
| Standard | GB/T 1222 | JIS G4801 | EN 10083 | AISI/SAE/ASTM ASTM A29 |
| Grade | 60CrMnA | SUP9A | / | 5160 |
4: AISI 5160 Steel Chemical Composition
| Grade | C | Si | Mn | P | S | Cr | V | Ni |
| 5160 | 0.56-0.64 | 0.15-0.3 | 0.75-1.0 | 0.035 | 0.040 | 0.7-0.9 | / | / |
5: AISI 5160 Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, please kindly contact the salesman.
6: AISI 5160 Steel Overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm | |
| Width 20mm-1000mm | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
7: AISI 5160 Steel Application
AISI 5160 steel is commonly used within industrial applications and within the automotive industry where robust and heavy duty springs are required.
8: AISI 5160 Steel Heat Treatment
Machinability
Machining 5160 alloy steel is difficult in “as rolled” condition. Hence, the steel should be annealed before machining to obtain maximum speeds.
Welding
AISI 5160 alloy steel has poor welding property owing to its high chromium and carbon content. Either arc or gas welding methods can be used to weld the steel.
Heat Treatment
AISI 5160 alloy steel is generally hardened using oil. This steel is quenched at 829°C (1525°F) and tempered at temperatures ranging from 427 and 704°C (800 and 1300°F).
Forging
Forging of 5160 alloy steel is performed at temperatures between 1149 and 1204°C (2100 and 2200°F).
Annealing
AISI 5160 alloy steel is annealed at 788°C (1450°F) and then air cooled.
9: AISI 5160 Steel Delivery condition
For hot rolled bar or hot rolled sheet, usually the delivery condition is hot rolled, annealed, black surface.